Cell thicknesses for Madey expt. Sept. 2000 - April 2001
Loop1 was deuterium
Loop2 was Hydrogen
convention is (theta in degrees with 0 deg at top going ccw, 
r in mm from center) and the thickness in 1/1000 inches

           0

   60              300


  120              240


          180

ie an entry like
120,1  4.44
means at a radius of 1mm from the center, at 120 degrees, 
the thickness measured was 4.44 mils.
                
Loop1 4cm entrance
0,0    4.29
0,1    4.40
60,1   4.59
120,1  4.59
180,1  4.5
240,1  4.59
300,1  4.40
0,2    4.5
60,2   4.5
120,2  4.5
180,2  4.5
240,2  4.5
300,2  4.5
0,3    4.29
60,3   4.29
120,3  4.29
180,3  4.29
240,3  4.29
300,3  4.29


Loop1 15cm Entrance
0,0    4.11
0,1    4.41
60,1   4.41
120,1  4.41
180,1  4.30
240,1  4.41
300,1  4.41
0,2    4.41
60,2   4.50
120,2  4.50
180,2  4.50
240,2  4.50
300,2  4.50

Loop2 15cm Entrance A1
0,0    5.2
0,1    5.0
60,1   5.2
120,1  4.9
180,1  4.9
240,1  4.9
300,1  4.9
0,2    5.0
60,2   5.0
120,2  5.0
180,2  5.0
240,2  5.0
300,2  5.0

Loop2 15cm Exit B1
0,0    5.1
0,1    5.8
60,1   5.8
120,1  5.8
180,1  5.8
240,1  5.9
300,1  5.8
0,2    6.0
60,2   6.0
120,2  6.0
180,2  6.0
240,2  6.2
300,2  6.0

Loop1 15cm Exit B2
0,0    5.2
0,1    5.9
60,1   5.8
120,1  5.9
180,1  6.0
240,1  6.0
300,1  5.8
0,2    6.2
60,2   6.0
120,2  6.3
180,2  6.2
240,2  6.2
300,2  5.9

Loop1 4cm Exit B1
0,0    5.4
0,1    5.5
60,1   5.1
120,1  5.2
180,1  5.1
240,1  5.8
300,1  5.2
0,2    5.7
60,2   5.6
120,2  5.1
180,2  5.7
240,2  6.1
300,2  5.8

Loop2 4cm Exit A2
0,0    5.5
0,1    6.1
60,1   6.1
120,1  6.1
180,1  5.7
240,1  6.6
300,1  6.6
0,2    6.5
60,2   6.5
120,2  6.5
180,2  6.3
240,2  6.8
300,2  6.8

Loop2 4cm Entrance A1
0,0    5.5
0,1    5.8
60,1   5.8
120,1  5.7
180,1  5.7
240,1  5.8
300,1  5.6
0,2    5.8
60,2   5.8
120,2  5.7
180,2  5.7
240,2  5.8
300,2  5.7